Damage threshold dependence of optical coatings on substrate materials
-
摘要: 以电子束及电阻热蒸发镀制的TiO2、ZrO2、SiO2、MgF2、ZnS等单层膜及TiO2/SiO2多层膜为例,实验研究了熔石英(SiO2)、蓝宝石(Al2O3)以及氟化钙(CaF2)等不同基板材料对光学薄膜近红外激光损伤阈值的影响,结果发现,对单层膜及增透膜,基板材料对损伤阈值有较为显著的影响,其一般规律是阈值随基板热导率的提高而提高,而对高反膜,基板材料则无甚影响。文章结合体/面吸收研究以及损伤瞬态行为分析,用局部吸收导致热破坏这一机理,较好地解释了上述现象。Abstract: Damage threshold dependence on substrate materials was investigated of TiO2,ZrO2,SiO2,MgF2,ZnS single and TiO2/SiO2 multilayers.The results show that the damage threshold increases with increasing substrate thermal conductivity for single layers and AR coatings and remains the same for HR coatings.With the help of localized absorption measurement and in-situ damage process analysis,these phenomena were well correlated with local-absorption-initiated thermal damage mechanism.
-
Key words:
-
[1] NBS Spec,Publ,1988,Vo1,752,P,259 P,271 Vo1,746,P,429. [2] NBS Spec,Publ,1984,Vol,669,P,130 P,138 P,292;P,386. [3] A,F,Stewart,et al.Laser Induced Damage in Optical Mate-Rials,1988,NIST Spec,Publ,to be Published. [4] NBS Spec,Publ,1975,Vol,435,P,14. [5] Opt,Acta,1981,Vol,28,P,1401. [6] 《中国激光》,1989午,第16卷,第8期,第470页. [7] IEEE J,Q,E,1981,Yol,QE—17,P,1888. [8] Appl,Opt,1982,Yol,21,P,3249. [9] Thin Solid Films,1988,Vo1,162,P,127. [10] 吴周令 范正修 高扬 王之江,《红外研究》,1990年,待发表. [11] 吴周令 范正修 苏星 王之江,《光学学报》,1990年,待发表. [12] 《激光与红外》,1989年,第19卷,第3期,第23页. [13] Appl,Phys,A,1983,Vol,32,P,141. [14] Appl,Phys,A,1985,Vol,38,P,19. [15] J,A,P,1986,Vo 1,59,No,2,P,348. [16] 《光学学报》,1989年,第9卷,第8期,第741页. [17] 《光学学报》,1989年,第9卷,第7期,第630页. [18] A,H,Guentter,Poivate Communication. [19] Z,L,yyu,Z,X,Fan,Z,J,Wang,Laser Induced Damage in Opt-ical Materia1s,1988,NIST Spec,Publ,to be Published.
计量
- 文章访问数: 3148
- HTML全文浏览量: 733
- PDF下载量: 272
- 被引次数: 0