Experimental study about CO2 laser welding of galvanized sheet
-
1.
School of Mechanical & Electronic Engineering, Guangdong Polytechnic Univercity, Guangzhou 510635, China;
-
2.
School of Mechanical Engineering, South China University of Technology, Guangzhou 510641, China;
-
3.
State Key Laboratory of Advanced Design and Manufacture for Vehicle Body, Hunan University, Changsha 410082, China
-
Corresponding author:
GONG Jin-ke, gongjinke@163.net
;
-
Received Date:
2006-10-24
Accepted Date:
2007-01-24
-
Abstract
Based on many experiments of CO2 laser welding of zinc coated high strength steel to vehicle body,joint microstructure and stress-strain curve of specimen were acquired.In the course of experiments,the sort of welding protective gas was selected,the influence of technological parameter on material melting characteristic of deep penetration welding was analyzed.By adopting blowing side protective gas,the problem that gas hole was easy to form owed to evaporation of zinc and moisture of circumstances in laser welding was solved.The experimental result indicated that deep penetration laser welding could effectively avoid softening heat affecting zone,control the gas hole and restrain joint flaw of welding of zinc coated high strength steel by blowing side protective gas.
-
-
References
|
[1]
|
TIAN H B,LIN J P,LIU R T et al.A Review on ultra-light auto body and related forming technologies[J].Automotive Engineering,2005,27(3):381～384(in Chinese). |
|
[2]
|
CHEN T,WANG Zh Y,CHEN K.Laser materials processing technology applied in large scale autobody[J].China Mechanical Engineering 2002,13(1):8～11(in Chinese). |
|
[3]
|
CUI H Y,ZUO T Ch.CO2 laser-welding of zinc coated steel sheets[J].Transactions of the China Welding Institution,2004,25(5):67～74(in Chinese). |
|
[4]
|
WU Sh K,ZHANG Zh W,CAO N et al.Investigation on Ultrasonic crossjet for laser welding[J].Laser Technology,2006,30(2):145～147(in Chinese). |
|
[5]
|
ZHOU Y Y,HU Ch K,CHEN P F.The laser welding of the double-linked gear in automobile gear-box[J].Laser Technology,2004,28(4):445～448(in Chinese). |
|
[6]
|
TANG X H,ZHU H H,ZHU G F et al.Laser_induced plasma absorption and control for CO2 laser deep-penetration wlding[J].China Mechanical Engineering,2000,11(7):741～744(in Chinese). |
|
[7]
|
WANG H L,HUANG W L,ZHOU Zh Y et al.Laser welding of 8mm thick stainless steel plates[J].Chinese Journal of Lasers,2003,30(5):463～466(in Chinese). |
|
[8]
|
CHEN L,HU X Y,HU L J.Characteristics on laser beam welded high strength steel[J].Applied Laser,2003,23(1):19～22(in Chinese). |
|
[9]
|
LI L J.Modern laser material processing and equipment[M].Beijing:Beijing Institute of Technology Press,1993.213～214(in Chinese). |
-
-
Proportional views
-
Map
DownLoad: