The analysis of metal deposition and micro-crystallites deposited byusing CO2 laser from aqueous solution

  • Received Date: 2007-09-20
    Accepted Date: 2008-01-22
  • In order to study the mechanism of metal deposition from aqueous solution induced by low power CO2 laser irradiation,dynamic force microscope(DFM) was used to analyze the crystallite distribution and it's growth of Ag deposition.Electronic probe micro-analysis(EPMA) was adopted to analyze the metal deposition on the epoxy surface along the transverse and longitude directions,and X-ray diffraction(XRD) was used to analyze the crystal growth of Ag-Cu deposited by electroless-plating.Ag crystallites distribution and its growth varied with the technical parameters.The transverse deposition on the epoxy surface defined the width of metal deposition and the longitude deposition defined its thickness.Although the crystal lattice parameters of Cu deposited on Ag by electroless-plating changed little,the crystallites grew in direction of (111),(200) and (220) of crystal,because the impurity atom penetrated in the Cu layer in the deposition process.
  • 加载中
  • [1]

    KORDAS O,LEPPAVUORI S,GEORGE T F,et al.Palladium thin film deposition on polyimide by CW Ar+ laser radiation for electro-less copper plating[J].Thin Solid Films,2001,384(3):185-188.
    [2]

    KORDáS K,NáNAI L,BALI K,et al.Palladium thin film deposition from liquid precursors on polymers by projected excimer beams[J].Applied Surface Science,2000,168(1):66-70.
    [3]

    KOLEV K,JADIN A,BENBAKOURA S,et al.Excimer laser-induced modification in PMMA/Ni-acetylcetonate films for selective metallization[J].Applied Surface Science,1999,139(6):434-438.
    [4]

    HUA Zh Y,LUO W A.Surface analysis[M].Shanghai:Fudan University Press,1989:145-166(in Chinese).
    [5]

    CHEN C H,ZHEN J Sh,LIU J G.Research of CO2 laser-induced metal deposition from aqueous solution[J].Plating and Surface Finishing,2003,90(5):84-90.
    [6]

    CHEN C H.CO2 laser-induced Ag deposition on epoxy resin from aqueous solution[J].Journal of Huazhong Uinversity of Science and Technology,2003,31(3):108-110(in Chinese).
    [7]

    CHEN C H.The mechanism of CO2 laser-induced metal deposition from aqueous solution[J].Laser Technology,2005,29(4):383-385(in Chinese).
    [8]

    YU X H.Macromolecule chemistry[M].Nanjing:Nanjing University Press,1994:15-33(in Chinese).
    [9]

    CHEN C H.The research for adhesion of metal layer deposited on epoxy-resin board by CO2 laser-induced from aqueous solution[J].Laser Technology,2004,28(1):26-28(in Chinese).
    [10]

    YANG Y X.X-ray analysis[M].Beijing:Traffic University Press,1989:71-88(in Chinese).
  • 加载中
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Article views(4144) PDF downloads(327) Cited by()

Proportional views

The analysis of metal deposition and micro-crystallites deposited byusing CO2 laser from aqueous solution

  • 1. Department of Chemistry, Huazhong Normal University, Wuhan 430079, China;
  • 2. Department of Manufacture, Dong-Feng Motor Co. Ltd., Wuhan 430056, China

Abstract: In order to study the mechanism of metal deposition from aqueous solution induced by low power CO2 laser irradiation,dynamic force microscope(DFM) was used to analyze the crystallite distribution and it's growth of Ag deposition.Electronic probe micro-analysis(EPMA) was adopted to analyze the metal deposition on the epoxy surface along the transverse and longitude directions,and X-ray diffraction(XRD) was used to analyze the crystal growth of Ag-Cu deposited by electroless-plating.Ag crystallites distribution and its growth varied with the technical parameters.The transverse deposition on the epoxy surface defined the width of metal deposition and the longitude deposition defined its thickness.Although the crystal lattice parameters of Cu deposited on Ag by electroless-plating changed little,the crystallites grew in direction of (111),(200) and (220) of crystal,because the impurity atom penetrated in the Cu layer in the deposition process.

Reference (10)

Catalog

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return