Wear property of NiCoFeCrTi high entropy alloy coating by laser cladding
-
摘要: 为了提高45#钢的耐磨性能,采用CO2激光熔覆技术进行了NiCoFeCrTi高熵合金涂层的制备实验。采用X射线衍射仪、扫描电镜和能谱仪分别分析了高熵合金熔涂层的物相结构、显微组织和化学成分。结果表明,由于高熵效应,NiCoFeCrTi涂层具有简单的面心立方相结构;在NiCoFeCrTi高熵合金涂层的熔覆层和结合区中未发现微裂纹,说明高熵合金与45#钢基底的冶金结合较好;熔覆涂层的表面显微硬度远远高于基底,维氏硬度可以达到940HV,是基底的3倍;表面熔覆了NiCoFeCrTi高熵合金的45#钢样品的磨损体积损失为5.010-10m3/m,低于45#钢的8.110-10m3/m。激光熔覆技术制备的NiCoFeCrTi高熵合金涂层可以显著提高45#钢耐磨损性能,对涂层应用研究具有较大参考意义。Abstract: In order to improve the wear resistance of 45# steel, NiCoFeCrTi high entropy alloy coating was obtained by CO2 laser cladding on 45# steel. The phase structure, microstructure and chemical composition of NiCoFeCrTi high entropy alloy layer were analyzed by X-ray diffraction scanning electron microscope(SEM) and energy dispersive spectroscopy respectively. The result shows that the phase structure of NiCoFeCrTi high entropy alloy coating is face-centered cubic structure due to high-entropy effect. There are no micro-cracks in the cladding zone, the bounding zone and heat affected zone of NiCoFeCrTi high entropy alloy samples. The analysis of microstructure by SEM shows that the coating is metallurgically bonded to the substrate. The surface microhardness of NiCoFeCrTi high entropy alloys samples is up to 940HV, about 3 times that of the substrate. The wear volume loss of 45# steel sample with NiCoFeCrTi high entropy alloy coating is 5.010-10m3/m, less than 8.110-10m3/m of 45# steel. The results show that, NiCoFeCrTi high entropy alloy coating prepared by laser cladding technology can significantly improve the wear resistance of 45# steel and it is meaningful to coating applications.
-
Keywords:
- laser technique /
- high entropy alloy /
- CO2 laser /
- laser cladding /
- wear resistance
-
-
[1] SHIH H R, TEOH L G, LIN H Z, et al. Preparation and photoluminescence properties of Pr3+ ion-doped Ca2LaTaO6 phosphors[J]. Journal of Electronic Materials, 2014, 43(4):1091-1096.
[2] YEH J W, CHEN S K, LIN S J, et al. Nanostructured high-entropy alloys with multiple principal elements:novel alloy design concepts and outcomes[J]. Advanced Engineering Materials, 2004, 6(5):299-303.
[3] NOVAK T G, VORA H D, MISHRA R S, et al. Synthesis of Al0.5CoCrCuFeNi and Al0.5CoCrFeMnNi high-entropy alloys by laser melting[J]. Metallurgical and Materials Transactions, 2014, B45(5):1603-1607.
[4] YEH J W. Alloy design strategies and future trends in high-entropy alloys[J]. Journal of Metals,2013, 65(12):1759-1771.
[5] TANG Zh, GAO M C, DIAO H Y, et al. Aluminum alloying effects on lattice types, microstructures, and mechanical behavior of high-entropy alloys systems[J]. Journal of Metals, 2013, 65(12):1848-1858.
[6] DAOUD H M, MANZONI A, VLKL R, et al. Microstructure and tensile behavior of Al8Co17Cr 17Cu8Fe17Ni33 (at.%) high-entropy alloy[J]. Journal of the Minerals Metals Materials Society, 2013, 65(12):1805-1814.
[7] LI Q H, YUE T M, GUO Z N, et al. Microstructure and corrosion properties of AlCoCrFeNi high entropy alloy coatings deposited on AISI 1045 steel by the electrospark process[J]. Metallurgical and Materials Transactions, 2013,A44(4):1767-1778.
[8] YEH A, CHANG Y, TSAI C, et al. On the solidification and phase stability of a Co-Cr-Fe-Ni-Ti high-entropy alloy[J]. Metallurgical and Materials Transactions, 2014, A45(1):184-190.
[9] WANG K, SUN G, ZHANG W, et al. Wear-corrosion properties of laser alloyed Mn-Al2O3 and Mn-Al2O3-NiWC layers[J]. Laser Technology, 2015, 39(2):274-279 (in Chinese).
[10] QUAN X,DING L,WEI X. Analysis of temperature field of laser cladding Ni-based alloy[J]. Laser Technology, 2013, 37(4):547-550 (in Chinese).
[11] LIN C,REN J,HE C. Microstructure of in-situ synthesized chromium carbide Ni-base composite coating by laser cladding[J]. Laser Technology, 2014, 38(2):186-190 (in Chinese).
[12] WANG Y, MA S, CHEN X, et al. Optimizing mechanical properties of AlCoCrFeNiTix high-entropy alloys by tailoring microstructures[J]. Acta Metallurgica Sinica (English Letters), 2013, 26(3):277-284.
[13] TONG C, CHEN Y, YEH J, et al. Microstructure characterization of AlxCoCrCuFeNi high-entropy alloy system with multiprincipal elements[J]. Metallurgical and Materials Transactions, 2005, A36(4):881-893.
[14] ARCHARD J F. Contact and rubbing of flat surfaces[J]. Journal of Applied Physics, 1953, 24(8):981-989.
-
期刊类型引用(16)
1. 蒋成成，宋庆雷，张平，柳学强，沈承金. 等离子熔覆FeCoCrNiAl_(0.5)Ti_(0.5)高熵合金涂层的组织及耐磨性能. 机械工程材料. 2024(10): 1-8 . 
百度学术
2. 张世钦，周娟，刘弘，朱永刚，蒋兆煌，孔令昊. 27SiMn钢表面激光熔覆FeCoCrNiMo_(0.75)高熵合金涂层组织与耐磨性能. 机械工程师. 2024(11): 95-98 . 百度学术
3. 王伟，陈田慧，单旭光，毕志江，刘伊，刘康诚，周吉，娄丽艳，李成新. 激光熔覆高熵合金涂层组织结构及强化机理研究进展. 热喷涂技术. 2023(04): 31-51 . 百度学术
4. 夏铭，孙博，王鑫，梁秀兵，沈宝龙. 高熵合金增材制造研究现状与展望. 材料导报. 2021(13): 13119-13127 . 百度学术
5. 张志虎，孙文磊，黄勇，刘金朵. 高速激光熔覆和重熔复合技术制备铁基涂层的组织性能研究. 激光与光电子学进展. 2021(21): 206-213 . 百度学术
6. 张富祯，孙文磊，王恪典，张冠. 面向薄壁件的激光熔覆修复工艺参数优化研究. 表面技术. 2019(01): 168-174 . 百度学术
7. 何昱煜，刘益剑，陈明，黄无云，戴鑫，毛建良，徐泽玮. 激光扫描速率与熔覆层组织性能的规律研究. 激光技术. 2019(02): 201-204 . 本站查看
8. 魏民，万强，李晓峰，朱方涛，黄永俊，杨兵. 熔覆电流对FeCoCrNiMn高熵合金涂层组织与性能的影响. 表面技术. 2019(06): 138-143 . 百度学术
9. 李凌宇，石岩，李镇. 激光沉积铁基涂层微观组织与耐磨性能研究. 长春理工大学学报(自然科学版). 2018(04): 25-30 . 百度学术
10. 谢锐波，廖一峰. 复合镀层激光热处理过程汽车模具配件磨损性能测试. 激光杂志. 2018(09): 82-85 . 百度学术
11. 刘鹏良，孙文磊，王恪典，黄海博. 扫描速率对激光熔覆镍基合金涂层性能的影响. 激光技术. 2018(06): 845-848 . 本站查看
12. 向硕，张雷，刘学，乐国敏，戴晓军，李强，李晋锋. 激光熔化沉积工艺对CrMnFeCoNi高熵合金组织和性能的影响. 材料热处理学报. 2018(10): 29-35 . 百度学术
13. 邱星武，刘春阁，张云鹏. 激光熔覆Al_2CoCrCuFeNi_xTi高熵合金涂层的组织及性能. 激光与光电子学进展. 2017(05): 267-273 . 百度学术
14. 黄海博，孙文磊，黄勇，陈影. 自由曲面熔覆路径的点云切片算法研究. 激光技术. 2017(05): 718-722 . 本站查看
15. 陈顺高，张晓明，郑启池，李瑞峰. CeO_2对激光熔覆Ni60合金涂层组织及性能的影响. 激光技术. 2017(06): 904-908 . 本站查看
16. 杨钢，严继康. 2016年云南金属材料与加工年评. 云南冶金. 2017(02): 86-104 . 百度学术
其他类型引用(14)
计量
- 文章访问数: 10
- HTML全文浏览量: 0
- PDF下载量: 5
- 被引次数: 30
下载: