Spectroscopic properties of Er3+ doped niobate-tellurite glasses

  • 1.

    Opto-electronic Technology Institute, Dalian Maritime University, Dalian 116026, China

  • Received Date: 2004-02-16
    Accepted Date: 2004-04-02
  • Er3+ doped niobate-tellurite glasses(EDTNb) are prepared, whose host compositions are TeO2,Nb2O5,ZnO and Na2O.The di fferential thermal analysis (DTA) curves of the glasses show that the thermal stability of EDTNb glasses against crystallization increases due to the introducti on of 4% Nb2O5.The measured absorption spectra are analyzed by McCumber theo ries in order to obtain the spectroscopic properties of the glasses.It is found that the peak stimulated emission crosssection of EDTNb glasses is 8.9×10-21cm2, which is 8% larger than that of tellurite glasses.
  • 加载中
  • [1]

    WANG J S,VOGEL E M,SNIZER E.Tellurite glass:a new candidate for fiber devices[J].Opt Mater,1994,3(4):187～203.
    [2]

    KOLOBKOVA E V,LIPOVSKII A A,MONTETOC J et al.Formation and modelling of optically waveguiding structures in a high-concentration Er-doped phosphate glass[J].J Phys,1999,D32L:9～12.
    [3]

    McCUMBER D E.Theory of phonon-terminated optical masers[J].Phys Rev,1964,A134(2):299～306.
    [4]

    MINISCALCO W J,QUIMBY R S.General procedure for the analysis of Er3+ cross sections[J].Opt Lett,1991, 16(4):258～260.
    [5]

    ROLLI R,MONTAGNA M.Erbium-doped tellurite glasses with high quantum efficiency and broadband stimulated emission cross section at 1.5μm[J].Opt Mater,2003, 21(4):743～748.
    [6]

    CHOI Y G,LIM D S,KIM K H et al.Enhanced 4I11/2→4I13/2 transition rate in Er3+/Ce3+-codoped tellurite glasses[J].Electron Lett,1999,35(20):1765～1767.
  • 加载中
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索
Get Citation
PDF
XML

Article views(2635) PDF downloads(357) Cited by()

Proportional views

Spectroscopic properties of Er3+ doped niobate-tellurite glasses

  • 1. Opto-electronic Technology Institute, Dalian Maritime University, Dalian 116026, China
  • Received Date: 2004-02-16
  • Accepted Date: 2004-04-02
  • Available Online: 2005-03-25

Abstract: Er3+ doped niobate-tellurite glasses(EDTNb) are prepared, whose host compositions are TeO2,Nb2O5,ZnO and Na2O.The di fferential thermal analysis (DTA) curves of the glasses show that the thermal stability of EDTNb glasses against crystallization increases due to the introducti on of 4% Nb2O5.The measured absorption spectra are analyzed by McCumber theo ries in order to obtain the spectroscopic properties of the glasses.It is found that the peak stimulated emission crosssection of EDTNb glasses is 8.9×10-21cm2, which is 8% larger than that of tellurite glasses.

    HTML

Reference (6)

Catalog

    Copyright © Laser Technology. 蜀ICP备10038222号-1

    Address：No. 7, Section 4, Renmin South Road, Chengdu, Sichuan Province, China Postal Code：610041  Telephone：028-68011091/68011046  Email： jgjs@vip.163.com,  jgjs@sina.com

    Supported by: Beijing Renhe Information Technology Co. Ltd  support: info@rhhz.net

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return