Preparation of durable hydrophobic and antireflective silica coating
-
1.
Research Center of Laser Fusion, China Academy of Engineering Physics, Mianyang 621900, China;
-
2.
School of Physical Electronics, University of Electronic Science and Technology of China, Chengdu 610054, China
-
Received Date:
2009-06-23
Accepted Date:
2009-08-13
-
Abstract
To improve the durable hydrophobicity of sol-gel silica antireflective coating,methyl-modified silica sol was prepared through hydrolysis and condensation of tetraethoxysilane and methyhriethoxysilane under ammonia catalysis in ethanol solvent.Then the sol was dip-coated onto both sides of clean K9 glass substrate to form single layer coatings.The chemistry of coating was analyzed by FF-IR spectroscopy,the water contact angle of coating was measured by contact measurement,the transmittance of coating was measured by spectrophotometer,and the thickness and refractive index of coating were measured by spectroscopic ellipsometry.More importantly,the durability of hyddropobicity of hydrophobic coating was reported for the first time.The results showed that coatings gained water repellence and antireflectivity at the same time by introducing CH3 into Si-O-Si linkage.The peak transmittance of the coating was above 99.5%; the static water contact angle was 130°,and the hydropobicity of such coating could last for 5 months in environment with relative humidity of 90%.
-
-
References
|
[1]
|
LIA A K,WANG Z M,LIU J J,et al.Study on the densification of SiO2-TiO2 sol-gel films by laser irradiation[J].Laser Technology,2008,32(4):343-349 (in Chinese). |
|
[2]
|
CHEN K,WU W P,ZHENG S X.Study on ammonia-sensitive optical property of ZnO/TiO2 multi-layer thin film[J].Laser Technology,2001,25(3):209-213(in Chinese). |
|
[3]
|
ZHU Y N.Discussion of the measurement methods for laser induced damage threshold of optical coating[J].Laser Technology,2006,30(5):532-535(in Chinese). |
|
[4]
|
YAN L H,CHI F T,JIANG X D,et al.Preparation of hydro-oleophobic silica antireflective coating[J].Journal of Inorganic Materials,2007,22(6):1247-1250(in Chinese). |
|
[5]
|
XIAO B,ZENG J F,CAO C R,et al.Preparation and characterization of polyoxidepropylene modified SiO2 antireflective film[J].Chinese Journal of Inorganic Chemistry,2008,24(3):491-494(in Chinese). |
|
[6]
|
CAO C R,NAN F,CHEN N,et al.Preparation and characteration of polyvinyl butyral doped organic-inorganic hybrid silica antireflective coatings[J].Chinese Journal of Inorganic Chemistry,2008,24(7):1104-1107(in Chinese). |
|
[7]
|
XU Y,WU D,SUN Y H,et al.Comparative study on hydrophobic antireflective films from three kinds of methyl-modified silica sols[J].Journal of Non-Crystalline Solids,2005,351:258-266. |
|
[8]
|
MA J H,WU G M,CHENG Y B,et al.Preparation of hydrophobic optical silica thin film with sol-gel method[J].Acta Physico-Chimica Sinica,2001,17(12):1112-1116(in Chinese). |
|
[9]
|
WANG J,ZHANG C R,FENG J,et al.Preparation and infrared spectral analysis of nanoporouos silica thin film[J].Spectroscopy and Spectral Analysis,2005,25(7):1045-1048(in Chinese). |
|
[10]
|
JIANG H M,ZHENG Z,WANG X L.Kinetic study of methyltriethoxysilane (MTES) hydrolysis by FTIR spectroscopy under different temperatures and solvents[J].Vibrational Spectroscopy,2008,46(1):1-7. |
|
[11]
|
ZHANG Q Y,WANG J,WU G,et al.Interence coating by hydrophobic aerogel-like SiO2 thin films[J].Materials Chemistry and Physics,2001,72(1):56-59. |
-
-
Proportional views
-
Map
DownLoad: