Microstructure and property of rotary double-focus laser-TIG hybrid welding of 304# stainless steel
-
1.
School of Mechanical Engineering and Automation, Beijing University of Aeronautics and Astronautics, Beijing 100083, China
-
Corresponding author:
WANG Su, wangsu@buaa.edu.cn
;
-
Received Date:
2008-09-11
Accepted Date:
2008-11-10
-
Abstract
In order to improve the property of stainless steel welding,a rotary double-focus laser-tungsten inert gas (TIG) hybrid welding technique was proposed,in which the rotary double-laser beam and the TIG arc were applied in welding at the same time.The rotary double-focus laser-TIG hybrid welding torch was designed,and a detailed experiment of rotary double-focus laser-TIG hybrid welding on the 304# stainless steel plate with different welding parameters was carried out.The results showed that the hybrid function between the double-focus laser and arc was the main factors affecting the microstructure of welded joint,and that the rotation frequency affected the mierostructure and micro-hardness of welded joint,the lower the rotary frequency,the higher the hardness because of smaller microstructure induced by re-melting of the welding line.The results are applicable in theoretical analysis and experimental research of laser-TIG hybrid welding technique.
-
-
References
|
[1]
|
BAGGER C,OLSEN F O.Review of laser hybrid welding[J].Journal of Laser Application,2005,17(1):2-14. |
|
[2]
|
TUSEK J,SUBAN M.Hybrid welding with arc and laser beam[J].Science and Technology of Welding and Joining,1999,4(5):308-311. |
|
[3]
|
HU Sh S,ZHANG Sh B,ZHAO J R.Arc augmented laser welding[J].Transactions of the China Welding Institution,1993,14(3):159-163(in Chinese). |
|
[4]
|
HARTFORD E.Stainless steel welding[M].Beijing:Chemical Industry Press,2004:56-68(in Chinese). |
|
[5]
|
ZHAO L,CHEN W Zh,ZHANG X D.Microstructure and mechanical properties of laser welded joint of NULCB steel[J].Laser Technology,2006,30(4):344-346(in Chinese). |
|
[6]
|
ZHANG X D,CHEN W Zh.Microstructures and toughness of weld metal of ultrafine grained ferritic steel by laser welding[J].Journal of Materials Science Technology,2004,20(6):755-759(in Chinese). |
|
[7]
|
ZHAO L,ZHANG X D,CHEN W Zh.CGHAZ microstructure andproperties of RPC steel laser welding[J].Transactions of the China Welding Institution,2005,26(6):131-135(in Chinese). |
|
[8]
|
YIN C Q,ZA X Zh,LU B Zh.Granular bainite in microstructures after welding and its effects on impact toughness in STE355 steel[J].Transactions of the China Welding Institution,2003,24(2):55-58(in Chinese) |
-
-
Proportional views
-
Map
DownLoad: